'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC 223R-111 SABIC INNOVATIVE CHONGQING
208
Form：Granules | Grade：Injection grade
Properties:
Flame retardantUV resistance
Typical Applications:
Automotive sectorElectrical appliancesPlastic bagLighting applicationsElectronic fieldElectrical field
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Automotive sector | Electrical appliances | Plastic bag | Lighting applications | Electronic field | Electrical field |
| Properties: | Flame retardant | UV resistance |
Certificates
No Data...
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| transmissivity | 2540 μm | ASTM D1003 | 88.0 | % |
| turbidity | 2540 μm | ASTM D1003 | 1.0 | % |
| Refractive index | ASTM D542 | 1.586 | ||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of cantilever beam gap | ASTM D1822 | 546 | kJ/m² | |
| Dart impact | 23°C | ASTM D3029 | 169 | J |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 | J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 | |
| -30°C | ISO 179/1eU | 无断裂 | ||
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 | kJ/m² |
| -30°C | ISO 179/1eA | 12 | kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C5 | ISO 180/1U | 无断裂 | |
| -30°C5 | ISO 180/1U | 无断裂 | ||
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 6.0 mm | UL 94 | V-0 | |
| 0.75 mm | UL 94 | V-2 | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | ASTM D1044 | 10.0 | mg |
| bending strength | Yield, 50.0 mm Span | ASTM D790 | 93.0 | Mpa |
| Bending modulus | 50.0 mm Span | ASTM D790 | 2340 | Mpa |
| elongation | Break | ASTM D638 | 110 | % |
| Yield | ASTM D638 | 7.0 | % | |
| tensile strength | Break | ASTM D638 | 65.0 | Mpa |
| Yield | ASTM D638 | 62.0 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 120 | °C | ||
| drying time | 3.0 to 4.0 | hr | ||
| Processing (melt) temperature | 280 to 305 | °C | ||
| Mold temperature | 70 to 95 | °C | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| Screw speed | 40 to 70 | rpm | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 to 60 | % | ||
| Temperature at the rear of the barrel | 260 to 280 | °C | ||
| Temperature in the middle of the barrel | 270 to 295 | °C | ||
| Temperature at the front of the material cylinder | 280 to 305 | °C | ||
| Spray nozzle temperature | 275 to 300 | °C | ||
| Exhaust hole depth | 0.025 to 0.076 | mm | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 137 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 132 | °C | |
| Vicat softening temperature | ASTM D15257 | 154 | °C | |
| Linear coefficient of thermal expansion | -40 to 95°C，Flow | ASTM E831 | 6.8E-5 | cm/cm/°C |
| specific heat | ASTM C351 | 1260 | J/kg/°C | |
| thermal conductivity | ASTM C177 | 0.25 | W/m/K | |
| RTI Elec | UL 746 | 100 | °C | |
| RTI Imp | UL 746 | 100 | °C | |
| RTI | UL 746 | 100 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Outdoor applicability | UL 746C | f1 | ||
| Water absorption rate | Equilibrium, 100°C | ASTM D570 | 0.58 | % |
| Equilibrium, 23°C | ASTM D570 | 0.35 | % | |
| 24 hr | ASTM D570 | 0.15 | % | |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 0.50 - 0.70 | % |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 18 | g/10 min |
| Specific volume | ASTM D792 | 0.830 | cm³/g | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | ASTM D257 | > 1.0E+17 | ohms·cm | |
| Dielectric strength | 3.20 mm, in Air | ASTM D149 | 15 | KV/mm |
| Dielectric constant | 60 Hz | ASTM D150 | 3.17 | |
| 50 kHz | ASTM D150 | 3.17 | ||
| 1 MHz | ASTM D150 | 2.96 | ||
| Dissipation factor | 50 Hz | ASTM D150 | 9.0E-4 | |
| 60 Hz | ASTM D150 | 9.0E-4 | ||
| 1 MHz | ASTM D150 | 0.010 | ||
| Compared to the anti leakage trace index | UL 746 | PLC 2 | ||
| High arc combustion index | UL 746 | PLC 1 | ||
| High voltage arc tracing rate | UL 746 | PLC 2 | ||
| Hot wire ignition | UL 746 | PLC 4 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Scale | ASTM D785 | 118 | |
| M-Scale | ASTM D785 | 70 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.