Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO1133 | 6.0 g/10min |
| Melt volume flow rate | | ISO1133 | 5.00 cm³/10min |
| Shrinkage rate | | ISO294-4 | 2.0 % |
| Water absorption rate | | ISO62 | 0.20 % |
| density | | ISO1183 | 1.42 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 150 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| burning rate | | FMVSS302 | <100 mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISOType | | ISO1874 | POM-K,M-GNS,02-002 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 2900 MPa |
| Tensile stress | Yield | ISO527-2/50 | 53.0 MPa |
| Bending stress | | ISO178 | 70.0 MPa |
| Tensile strain | Yield | ISO527-2/50 | 6.0 % |
| Tensile strain | Break | ISO527-2/50 | 13 % |
| Flexural modulus | | ISO178 | 2800 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 60 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180 | 4.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 25 kV/mm |
| dielectric constant | | IEC60250 | 4.00 |
| Surface Resistivity | | IEC60093 | 1E+14 ohms |
| Volume resistivity | | IEC60093 | 1E+14 ohms·cm |
| Dissipation Factor | | IEC60250 | 9.5E-03 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 100 °C |
| vicat | | ISO306/B | 140 °C |
| melting temperature | | ISO11357-3 | 167 °C |
| LimitTemperature-effect host operation | | | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.