ASA+PC GELOY™ XTPMFR10 resin
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| MeltViscosity | ISO 11443 | 105 Pa·s | |
| density | ISO 1183 | 1.18 g/cm³ | |
| Melt volume flow rate | ISO 1133 | 30.0 cm³/10min |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | Yield | ASTM D638 | 4.0 % |
| Tensile strain | Yield | ISO 527-2/5 | 4.0 % |
| Yield | ISO 527-2/50 | 4.0 % | |
| elongation | ASTM D638 | 58 % | |
| ASTM D638 | 31 % | ||
| Tensile strain | Break | ISO 527-2/5 | 50 % |
| Break | ISO 527-2/50 | 21 % | |
| Flexural modulus | ISO 178 | 2730 MPa | |
| tensile strength | Yield | ISO 527-2/5 | 61.0 MPa |
| Yield | ISO 527-2/50 | 66.0 MPa | |
| ASTM D638 | 49.0 MPa | ||
| ASTM D638 | 47.0 MPa | ||
| bending strength | ISO 178 | 97.0 MPa | |
| tensile strength | Break | ISO 527-2/5 | 46.0 MPa |
| Break | ISO 527-2/50 | 47.0 MPa | |
| Tensile modulus | ASTM D638 | 2680 MPa | |
| ISO 527-2/1 | 2680 MPa | ||
| tensile strength | Yield | ASTM D638 | 60.0 MPa |
| Yield | ASTM D638 | 65.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 13 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 90 J/m | |
| ASTM D256 | 330 J/m | ||
| ISO 180/1A | 12 kJ/m² | ||
| ISO 180/1A | 13 kJ/m² | ||
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 85.0 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Bf | 90.0 °C | |
| ISO 75-2/Af | 81.0 °C | ||
| vicat | ISO 306/B50 | 96.0 °C | |
| ISO 306/B120 | 98.0 °C | ||
| Linear coefficient of thermal expansion | ISO 11359-2 | 6.3E-05 cm/cm/°C | |
| ISO 11359-2 | 6.3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.