Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 0.910 g/cm³ |
| melt mass-flow rate | | ISO1133 | 11 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 76.0 MPa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ISO2813 | 100 |
| Haze ratio | | ASTMD1003 | 2.7 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| tear strength | | DIN53455 | 42.0 MPa |
| tear strength | | DIN53455 | 38.0 MPa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO527-2/50 | >50 % |
| Flexural modulus | | DIN53121 | 700 MPa |
| Flexural modulus | | DIN53121 | 670 MPa |
| | DIN53375 | 0.18 |
| Tensile modulus | | ISO527-2/1 | 1500 MPa |
| Tensile stress | Yield | ISO527-2/50 | 35.0 MPa |
| Tensile strain | Yield | ISO527-2/50 | 9.0 % |
| film | Test Condition | Test Method | Test Result |
|---|
| Film thickness - tested | | | 50 µm |
| elongation | | DIN53455 | 680 % |
| elongation | | DIN53455 | 720 % |
| Falling hammer impact | | ASTMD1709 | 280 g |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 85.0 °C |
| vicat | | ISO306/A50 | 154 °C |
| | ISO3146 | 163 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.