Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 2577 | 0.11 % |
| Shrinkage rate | | DIN 53464 | 0.0 % |
| Water absorption rate | | ISO 62 | <0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| fiber content | | ISO 1172 | 50 % |
| MaterialDesignation | | EN14598-1 | >UP-(GF+KD |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 12000 MPa |
| tensile strength | Break | ISO 527-2 | 160 MPa |
| Flexural modulus | | ISO 178 | 15000 MPa |
| bending strength | | ISO 178 | 380 MPa |
| Poisson's Ratio | | | 0.30 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | 170 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | | 140 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.2E-05 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/A | >200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.