POM Homopolymer 577 BK000

Properties:
Filler
glass fiber reinforced material
20%
filler by weight
Compare

Technical Data Sheet

physical property	Test Method	Test Result
Shrinkage rate	ISO 294-4	1.7 %
density	ISO 1183	1.56 g/cm³
Melt volume flow rate	ISO 1133	7.00 cm³/10min
Shrinkage rate	ISO 294-4	1.1 %

flammability	Test Condition	Test Method	Test Result
burning rate		ISO 3795	<100 mm/min
UL flame retardant rating		UL 94	HB
	UL flame retardant rating		UL 94	HB
		UL flame retardant rating		IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating		IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	4800 MPa
tensile strength	Break	ISO 527-2	52.0 MPa
Tensile strain	Break	ISO 527-2	10 %
Flexural modulus		ISO 178	4600 MPa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	3.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	3.0 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	164 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	118 °C
melting temperature		ISO 11357-3	178 °C
Linear coefficient of thermal expansion		ISO 11359-2	5.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	9.2E-05 cm/cm/°C
AnnealingTemperature			160 °C
AnnealingTime-Optional			30.0 min/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.