Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.14 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 1.3to1.7 % |
| Water absorption rate | | ASTM D570 | 10 % |
| Water absorption rate | | ASTM D570 | 1.8 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 750 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | ASTM D638 | 80.0 MPa |
| elongation | Break | ASTM D638 | 80 % |
| Flexural modulus | | ASTM D790 | 2600 MPa |
| bending strength | Break | ASTM D790 | 100 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 80 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 18 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 70.0 °C |
| vicat | | ASTM D15252 | 190 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.