PP POLYFLAM® RPP 2000 E A SCHULMAN USA

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3.5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	21	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	0.750mm,自动灭火	ISO 3795	0.0	mm/min
	Burning rate	1.50mm,自动灭火	ISO 3795	0.0	mm/min
	Burning rate	Burning rate	3.00mm,自动灭火	ISO 3795	0.0	mm/min
UL flame retardant rating	0.750mm	UL 94,IEC60695-11-10,-20	V-2
	UL flame retardant rating	1.50mm	UL 94,IEC60695-11-10,-20	V-2
	UL flame retardant rating	UL flame retardant rating	3.00mm	UL 94,IEC60695-11-10,-20	V-2
Burning wire flammability index	0.750mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.50mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.00mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.750mm	IEC 60695-2-13	750	°C
	Hot filament ignition temperature	1.50mm	IEC 60695-2-13	750	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.00mm	IEC 60695-2-13	750	°C
Extreme Oxygen Index		ISO 4589-2	27	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1A/1	1900	MPa
tensile strength	Yield	ISO 527-2/1A/50	38.0	MPa
Tensile strain	Yield	ISO 527-2/1A/50	8.0	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Imp	3.00mm	UL 746	65.0	°C
RTI	0.750mm	UL 746	65.0	°C
	RTI	1.50mm	UL 746	65.0	°C
	RTI	RTI	3.00mm	UL 746	65.0	°C
Ball Pressure Test	145°C	IEC 60695-10-2	Pass
RTI Elec	0.750mm	UL 746	65.0	°C
	RTI Elec	1.50mm	UL 746	65.0	°C
	RTI Elec	RTI Elec	3.00mm	UL 746	65.0	°C
RTI Imp	0.750mm	UL 746	65.0	°C
RTI Imp	RTI Imp	1.50mm	UL 746	65.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183/A	0.910	g/cm³
Melt Volume Flow Rate (MVR)	230°C/2.16kg	ISO 1133	2.00	cm³/10min
Water absorption rate	23°C,24hr	ISO 62	0.16	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+13	ohms·cm
Compared to the anti leakage trace index		IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.