Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.06 g/cm³ |
| density | | ISO1183 | 1.07 g/cm³ |
| melt mass-flow rate | | ISO1133 | 6.0 g/10min |
| Shrinkage rate | | 内部方法 | 0.50to0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 114 |
| Rockwell hardness | | ISO2039-2 | 114 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 41.0 Mpa |
| Tensile modulus | | ISO527-2/1 | 2500 Mpa |
| Tensile stress | | ISO527-2/50 | 48.0 Mpa |
| Tensile stress | | ISO527-2/50 | 39.0 Mpa |
| Nominal tensile fracture strain | | ISO527-2/50 | 28 % |
| Flexural modulus | | ASTMD790 | 2350 Mpa |
| Flexural modulus | | ISO178 | 2450 Mpa |
| | ASTMD790 | 75.0 Mpa |
| Bending stress | | ISO178 | 78.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 19 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 200 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/B | 115 °C |
| Hot deformation temperature 5 | | ASTMD648 | 106 °C |
| | ISO75-2/Af | 95.0 °C |
| vicat | | ASTMD15256 | 116 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare