PPA Laramid G/15
0
- Properties:Fillerglass fiber reinforced material15%filler by weight
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.30 g/cm³ | |
| Shrinkage rate | ISO294-4 | 0.85to1.2 % | |
| ISO294-4 | 0.40to0.70 % | ||
| Water absorption rate | ISO62 | 0.21 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179/1eU | 20 kJ/m² | |
| Charpy Notched Impact Strength | ISO179/1eA | 4.0 kJ/m² | |
| ISO179/1eA | 4.0 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO179/1eU | 17 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | ISO527-2/5 | 110 MPa | |
| ISO527-2/5 | 105 MPa | ||
| ISO527-2/5 | 100 MPa | ||
| ISO527-2/5 | 75.0 MPa | ||
| ISO527-2/5 | 55.0 MPa | ||
| Tensile strain | ISO527-2/5 | 3.5 % | |
| ISO527-2/5 | 10 % | ||
| Tensile stress | ISO527-2/5 | 80.0 MPa | |
| Tensile strain | ISO527-2/5 | 2.0 % | |
| ISO527-2/5 | 5.0 % | ||
| ISO527-2/5 | 12 % | ||
| Tensile stress | ISO527-2/5 | 55.0 MPa | |
| Tensile modulus | ISO527-2/1 | 7200 MPa | |
| ISO527-2/1 | 6800 MPa | ||
| ISO527-2/1 | 5700 MPa | ||
| ISO527-2/1 | 4400 MPa | ||
| ISO527-2/1 | 2000 MPa | ||
| Tensile strain | ISO527-2/5 | 2.0 % | |
| ISO527-2/5 | 2.0 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/B | 280 °C | ||
| ISO75-2/A | 250 °C | ||
| Continuous use temperature | 135 °C | ||
| vicat | ISO306/B50 | 265 °C | |
| ISO11359-2 | 2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.