Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO1183 | 1.36 g/cm³ |
Water absorption rate | | ISO62 | 6.00 % |
Water absorption rate | | ISO62 | 2.10 % |
hardness | Test Condition | Test Method | Test Result |
---|
| | ISO2039-1 | 181 Mpa |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Impact strength of cantilever beam gap | | ISO180/1A | 10 kJ/m² |
Impact strength of cantilever beam gap | | ISO180/1A | 8.4 kJ/m² |
tensile strength | | ISO527-2 | 180 Mpa |
elongation at break | | ISO527-2 | 3.0 % |
Tensile modulus | | ISO527-2 | 9500 Mpa |
Flexural modulus | | ISO178 | 8600 Mpa |
Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
Flame retardant performance | Test Condition | Test Method | Test Result |
---|
fire rating | | UL-94 | 1.50mm HB |
fire rating | | UL-94 | 2.00mm HB |
fire rating | | UL-94 | 3.00mm HB |
GWIT | | IEC60695-2-12 | 750 °C |
GWIT | | IEC60695-2-12 | 800 °C |
GWIT | | IEC60695-2-12 | 750 °C |
Relative temperature of heating wire | | IEC60695-2-13 | 725 °C |
Relative temperature of heating wire | | IEC60695-2-13 | 775 °C |
Relative temperature of heating wire | | IEC60695-2-13 | 725 °C |
Electrical performance | Test Condition | Test Method | Test Result |
---|
| | IEC60093 | 1E+13 Ω.cm |
dielectric constant | | IEC60250 | 3.80 1MHz |
Dissipation Factor | | IEC60250 | 0.025 100HZ |
Dissipation Factor | | IEC60250 | 0.025 1MHz |
Dissipation Factor | | IEC60112 | 550 V |
Thermal performance | Test Condition | Test Method | Test Result |
---|
| | ISO75-2/Bf | 220 °C |
| | ISO75-2/Af | 210 °C |
vicat | | ISO11357-3 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.