AES DIALAC® SK30 UMG JAPAN
827
- Properties:Glass fiber reinforced
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 20 | CM | ||
| Melt Volume-Flow Rate (MVR) | 220°C/10.0kg | ISO1133 | 20.0 | cm3/10min |
| Shrinkage rate | MD：23°C | ISO294-4 | 0.60到0.80 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO2039-2 | 103 | |
| Tensile modulus | 23°C | ISO527-2 | 2300 | Mpa |
| tensile strength | 23°C | ISO527-2 | 45.0 | Mpa |
| Bending modulus | 23°C | ISO178 | 2450 | Mpa |
| Bending stress | 23°C | ISO178 | 73.0 | Mpa |
| Impact strength of simply supported beam gap | 15 | KJ/m | ||
| Bending modulus | 2450 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 81 | °C | ||
| Flame retardant grade | UL94 | HB | ||
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/Af | 81.0 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.