'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
ABS MG47F NA1000 SABIC INNOVATIVE SAUDI
316
Form：Granules
Properties:
High toughnessLow temperature resistancHigh impact resistanceHigh gloss
Typical Applications:
small home appliances
Product Description
Certificates(0)
Datasheet
Alternative(3)
Product Description
| Typical Applications: | small home appliances |
| Properties: | High toughness | Low temperature resistanc | High impact resistance | High gloss |
Certificates
No Data...
Technical Data Sheet
| Filling analysis | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Melt viscosity | 240°C, 1000 sec^-1 | ASTM D3835 | 225 | Pa·s |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 30.0 | J |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 26 | kJ/m² |
| -30°C | ISO 179/1eA | 9.0 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5 mm | UL 94 | HB | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | --1 | ASTM D638 | 2270 | Mpa |
| -- | ISO 527-2/1 | 2370 | Mpa | |
| tensile strength | Yield2 | ASTM D638 | 44.0 | Mpa |
| Yield | ISO 527-2/50 | 47.0 | Mpa | |
| Break2 | ASTM D638 | 33.0 | Mpa | |
| Break | ISO 527-2/50 | 35.0 | Mpa | |
| elongation | Yield2 | ASTM D638 | 2.0 | % |
| Yield | ISO 527-2/50 | 2.6 | % | |
| Break2 | ASTM D638 | 24 | % | |
| Break | ISO 527-2/50 | 25 | % | |
| Bending modulus | 50.0 mm Span3 | ASTM D790 | 2300 | Mpa |
| bending strength | Yield, 50.0 mm Span3 | ASTM D790 | 70.0 | Mpa |
| --4,5 | ISO 178 | 70.0 | Mpa | |
| Bending modulus | --4 | ISO 178 | 2200 | Mpa |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 80 to 95 | °C | ||
| drying time | 2.0 to 4.0 | hr | ||
| Suggested maximum moisture content | 0.10 | % | ||
| Suggested injection volume | 50 to 70 | % | ||
| Temperature at the rear of the barrel | 190 to 210 | °C | ||
| Temperature in the middle of the barrel | 205 to 225 | °C | ||
| Temperature at the front of the material cylinder | 215 to 240 | °C | ||
| Spray nozzle temperature | 220 to 260 | °C | ||
| Processing (melt) temperature | 220 to 260 | °C | ||
| Mold temperature | 50 to 70 | °C | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| Screw speed | 30 to 60 | rpm | ||
| Exhaust hole depth | 0.038 to 0.051 | mm | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| RTI | UL 746 | 60.0 | °C | |
| RTI Imp | UL 746 | 60.0 | °C | |
| RTI Elec | UL 746 | 60.0 | °C | |
| Linear coefficient of thermal expansion | Across Flow : -40 to 40°C | ASTM E831 | 8.8E-5 | cm/cm/°C |
| Flow : -40 to 40°C | ASTM E831 | 8.8E-5 | cm/cm/°C | |
| Vicat softening temperature | -- | ISO 306/B120 | 100 | °C |
| -- | ISO 306/B50 | 98.0 | °C | |
| -- | ASTM D15258 | 99.0 | °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7 | ISO 75-2/Af | 81.0 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 80.0 | °C | |
| 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 94.0 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| melt mass-flow rate | 230°C/3.8 kg | ASTM D1238 | 5.6 | g/10 min |
| 220°C/10.0 kg | ISO 1133 | 18 | g/10 min | |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 0.50 - 0.80 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Arc resistance | ASTM D495 | PLC 6 | ||
| Hot wire ignition | UL 746 | PLC 3 | ||
| High voltage arc tracing rate | UL 746 | PLC 3 | ||
| High arc combustion index | UL 746 | PLC 0 | ||
| Compared to the anti leakage trace index | UL 746 | PLC 0 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Scale | ASTM D785 | 112 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.