Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.18 g/cm³ |
| melt mass-flow rate | | ISO1133 | 15 g/10min |
| Water absorption rate | | ISO62 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 85 |
| | ISO2039-1 | 175 MPa |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542,ISO489 | 1.490 |
| transmissivity | | ASTMD1003 | 92.0 % |
| Haze ratio | | ASTMD1003 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 650 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | ISO178 | 105 MPa |
| Tensile stress | Yield | ISO527-2 | 75.0 MPa |
| Tensile strain | Yield | ISO527-2 | 4.0 % |
| Flexural modulus | | ISO178 | 2900 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 18 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 1.7 kJ/m² |
| Dart impact equipped with measuring instruments | | ASTMD3763,ISO6603-2 | 0.300 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD696 | 7.1E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.