Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Chlorine content | | ISO1158 | 65.0 wt% |
| density | | JISK7112 | 1.54 g/cm³ |
| Apparent density | | JISK6720-2 | 0.50到0.60 g/cm³ |
| K-Value | | JISK6720-2 | 58.0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Temperature Flex | | JISK6745 | 88 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Yield | JISK7113 | 59.0 MPa |
| Tensile strain | Break | JISK7113 | 50 % |
| Flexural modulus | | JISK7171 | 2750 MPa |
| Bending stress | | JISK7171 | 86.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | JISK7111 | 20 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | | 1E+15 ohms·cm |
| dielectric strength | | | 47到63 kV/mm |
| dielectric constant | | | 3.08 |
| dielectric constant | | | 3.20到3.60 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | JISK7207 | 97.0 °C |
| | JISK7191-1 | 87.0 °C |
| vicat | | JISK7206 | 104 °C |
| | ASTMD696 | 7.0E-5到7.5E-5 cm/cm/°C |
| | JISK6720-2 | <0.3 wt% |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.