PBT 7151G-X01 TORAY SHENZHEN

Form：Granules | Grade：Injection grade

Properties:

Low warpagelow densityFiller: Glass fiber reinflow densityLow warpage30% filler by weight

Typical Applications:

Automotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive sector
Properties:	Low warpage \| low density \| Filler: Glass fiber reinf \| low density \| Low warpage \| 30% filler by weight

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield, 23℃	ISO 527-2	130	Mpa
Tensile strain	Break, 23℃	ISO 527-2	2.3	%
Charpy Notched Impact Strength	23℃	ISO 179	9.5	kJ/m²
Tensile modulus	23°C	ISO 527-2	10000	Mpa
tensile strength	23°C	ISO 527-2	135	Mpa
Tensile strain	Break,23°C	ISO 527-2	2.2	%
Bending modulus	23°C	ISO 178	10000	Mpa
bending strength	23°C	ISO 178	190	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
0.45MPa, unannealed		ISO 75-2/B	209	°C
1.8MPa, unannealed		ISO 75-2/A	163	°C
Linear coefficient of thermal expansion	MD：-30to100°C	ISO 11359-2	4.2E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD: 3.00 mm	Internal Method	0.50	%
	Shrinkage rate	MD: 3.00 mm	Internal Method	0.20	%
		Shrinkage rate	TD:3.00mm1	Internal Method	0.50	%
		Shrinkage rate	Shrinkage rate	MD:3.00mm2	Internal Method	0.20	%
Water absorption rate	23°C,24hr	ISO 62	0.090	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	3E+16	ohms·cm
Dielectric strength		IEC 60243-1	16	KV/mm
Dielectric constant	23°C,1kHz	IEC 60250	3.80
Dissipation factor	23°C,1MHz	IEC 60250	0.010

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.