Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.20 g/cm³ |
| Water absorption rate | | ISO 62 | 0.20 % |
| water content | | ISO 960 | <1000 ppm |
| Shrinkage rate | | | 1.0 % |
| Shrinkage rate | | | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/5 | 2250 MPa |
| tensile strength | | ISO 527-2/5 | 55.0 MPa |
| Tensile strain | | ISO 527-2/5 | >50 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180/1A | 25 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 55 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 无断裂 |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 90.0 °C |
| melting temperature | | ISO 11357 | 125 °C |
| Heat distortion temperature | | ISO 75-2/B | 110 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare