POP PT 1451G1
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTMD792 | 0.902 g/cm³ | |
| melt mass-flow rate | ISO1133 | 7.5 g/10min | |
| density | ASTM D792 | 0.902 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 7.5 g/10 min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | Yield | ISO 527-2 | 5.00 MPa |
| Tensile strain | Break | ISO 527-2 | 1000 % |
| Tensile stress | Yield | ISO527-2 | 5.00 MPa |
| Break | ISO527-2 | 20.0 MPa | |
| Tensile strain | Break | ISO527-2 | 1000 % |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Internal Method | 83.0 ℃ | ||
| Water vapor permeability | Internal Method | 390 g/m²/24 hr | |
| 内部方法 | 83.0 °C | ||
| Water vapor permeability | 内部方法 | 390 g/m²/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D1525 | 79.0 ℃ | |
| Internal Method | 98.0 ℃ | ||
| vicat | ASTMD1525 | 79.0 °C | |
| melting temperature | DSC | 98.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.