Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| saturation | | % | 7,9到11 |
| balance | | % | 2.5-3.5 |
| viscosity number | | cm³/g | 138to247 |
| balance | | % | 2.5 |
| melt mass-flow rate | | g/10min | 1.2-5.0 |
| flow | | mm/mm | 152.4E-3-0.635 |
| saturation | | % | 9.0 |
| Apparent density | | g/cm³ | 0.70-0.78 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | | 45.03to201.38 Mpa |
| Shore hardness | | | 77to80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | °C | 743to960 |
| Limiting Oxygen Index | | % | 21to28 |
| Burning wire flammability index | | °C | 954to960 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Nominal tensile fracture strain | | % | 5,6到50 |
| Tensile modulus | | | 477.24到0.01,0.04E0.05 Mpa |
| yield | | % | 3,0到21 |
| yield | | | 64.76to85.52 Mpa |
| fracture | | | 40.0to171.72 Mpa |
| fracture | | % | 3,0到77 |
| yield | | | 39.03to89.66 Mpa |
| coefficient of friction | | | 0.30-1.0 |
| fracture | | | 79.31to84.83 Mpa |
| fracture | | % | 2,2到12 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | kJ/m² | 1.988to6.176 |
| Charpy Notched Impact Strength | | kJ/m² | 0.556to4.643 |
| Impact strength of simply supported beam without notch | | kJ/m² | 10.679to23.215 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | 1.0E+2-2.5E+13 |
| Dissipation Factor | | | 0.020-0.30 |
| Volume resistivity | | | 3.50 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | °C | 67to247 |
| flow | | mm/mm/°C | 99.1E-5-101.6E-5 |
| Continuous use temperature | | °C | 87to202 |
| flow | | mm/mm/°C | 96.5E-5-152.4E-5 |
| horizontal | | mm/mm/°C | 99.1E-5-203.2E-5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.