Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.17 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 83 77 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | | V-2 -- |
| Hot filament ignition temperature | | °C | 960 -- |
| Limiting Oxygen Index | | % | 30 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | MPa | 75.0 40.0 |
| tensile strength | Break | MPa | 60.0 45.0 |
| Tensile strain | Break | % | 10 30 |
| Flexural modulus | | MPa | 3000 1000 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 3.0 10 |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Impact strength of cantilever beam gap | | kJ/m² | 3.0 10 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1E+15 1E+12 |
| dielectric strength | | kV/mm | 26 -- |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Surface Resistivity | | ohms | 1E+14 1E+12 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 65.0 -- |
| melting temperature | | °C | 220 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.