PA6 SCHULAMID® 6MV14 FR4 K1681
58
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| viscosity number | ISO 307 | 145 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 160 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 | |
| UL 94 | V-2 | ||
| IEC 60695-11-10,-20 | V-2 | ||
| IEC 60695-11-10,-20 | V-2 | ||
| IEC 60695-11-10,-20 | V-2 | ||
| IEC 60695-11-10,-20 | V-2 | ||
| Burning wire flammability index | IEC 60695-2-12 | 850 °C | |
| IEC 60695-2-12 | 850 °C | ||
| IEC 60695-2-12 | 960 °C | ||
| IEC 60695-2-12 | 960 °C | ||
| burning rate | ISO 3795 | 0.0 mm/min | |
| ISO 3795 | 0.0 mm/min | ||
| ISO 3795 | 0.0 mm/min | ||
| ISO 3795 | 0.0 mm/min | ||
| UL flame retardant rating | UL 94 | V-2 | |
| UL 94 | V-2 | ||
| Hot filament ignition temperature | IEC 60695-2-13 | 825 °C | |
| IEC 60695-2-13 | 825 °C | ||
| IEC 60695-2-13 | 825 °C | ||
| IEC 60695-2-13 | 825 °C | ||
| Limiting Oxygen Index | ISO 4589-2 | 23 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 3800 Mpa | |
| tensile strength | ISO 527-2/1A/50 | 70.0 Mpa | |
| Tensile strain | ISO 527-2/1A/50 | 3.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 48 kJ/m² | |
| ISO 179/1eU | 49 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| UL 746 | PLC 0 | ||
| UL 746 | PLC 0 | ||
| UL 746 | PLC 0 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 4 | |
| UL 746 | PLC 4 | ||
| UL 746 | PLC 2 | ||
| UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Bf | 186 °C | |
| ISO 75-2/Af | 76.0 °C | ||
| RTI Imp | UL 746 | 100 °C | |
| RTI Str | UL 746 | 100 °C | |
| UL 746 | 110 °C | ||
| UL 746 | 120 °C | ||
| UL 746 | 120 °C | ||
| vicat | ISO 306/A50 | 217 °C | |
| ISO 306/B50 | 202 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| RTI Elec | UL 746 | 130 °C | |
| UL 746 | 130 °C | ||
| UL 746 | 130 °C | ||
| UL 746 | 130 °C | ||
| RTI Imp | UL 746 | 75.0 °C | |
| UL 746 | 90.0 °C | ||
| UL 746 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.