| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 8.0 g/10min |
| Shrinkage rate | | ASTMD955 | 0.50to0.70 % |
| Water absorption rate | | ASTMD570 | 0.15 % |
| Water absorption rate | | ASTMD570 | 0.32 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 118 |
| Rockwell hardness | | ASTMD785 | 73 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542 | 1.586 |
| transmissivity | | ASTMD1003 | 89.0 % |
| Haze ratio | | ASTMD1003 | 0.70to1.5 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-2 |
| Hot filament ignition temperature 7 | | IEC60695-2-13 | 850 °C |
| Limiting Oxygen Index | | ASTMD2863 | 26 % |
| Average degree of combustion | | ASTMD635 | 3 CM |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2410 Mpa |
| tensile strength | | ASTMD638 | 60.0 Mpa |
| tensile strength | | ASTMD638 | 72.0 Mpa |
| elongation | | ASTMD638 | 6.0 % |
| elongation | | ASTMD638 | 150 % |
| Flexural modulus | | ASTMD790 | 2410 Mpa |
| bending strength | | ASTMD790 | 96.0 Mpa |
| | Kg/m | 45 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam gap impact strength 4 | | ASTMD256 | 900 J/m |
| Dart impact with measuring instruments 5 | | ASTMD3763 | 89.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 2E+17 ohms·cm |
| dielectric strength | | ASTMD149 | 17 KV/mm |
| dielectric constant | | ASTMD150 | 3.00 |
| Dissipation Factor | | ASTMD150 | 1E-03 |
| CTI | | IEC60112 | 250 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 144 °C |
| Heat distortion temperature | | ASTMD648 | 128 °C |
| Heat distortion temperature | | ASTMD648 | 141 °C |
| vicat | | ASTMD15256 | 150 °C |
| | IEC60598-1 | >125 °C |
| | ASTMD696 | 6.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.