ABS XR-407D CNOOC&LG HUIZHOU

Form：Granules | Grade：Injection grade

Properties:

High impact resistanceHigh temperature resistanHigh mobility

Typical Applications:

Electronic fieldElectrical fieldAutomotive sectorsmall home appliances

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electronic field \| Electrical field \| Automotive sector \| small home appliances
Properties:	High impact resistance \| High temperature resistan \| High mobility

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	200℃/5kg	ASTM D-1238	1	g/10min
	melt mass-flow rate	220℃/10kg	ASTM D-1238	7	g/10min
	melt mass-flow rate	melt mass-flow rate	230℃/3.8kg	ASTM D-1238	3	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield,50mm/min	ASTM D-638	450	kg/cm
Tensile modulus	1mm/min	ASTM D-638	23000	%
elongation at yield	50mm/min	ASTM D-638	8	%
Elongation at Break	50mm/min	ASTM D-638	20	%
bending strength	15mm/min	ASTM D-790	750	kg/cm
Bending modulus	15mm/min	ASTM D-790	25500	kg/cm
Impact strength of cantilever beam gap	1/4" 23℃	ASTM D-256	18	kg-cm/cm
	Impact strength of cantilever beam gap	1/4" -30℃	ASTM D-256	8	kg-cm/cm
		Impact strength of cantilever beam gap	1/8" 23℃	ASTM D-256	19	kg-cm/cm
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	1/8" -30℃	ASTM D-256	8	kg-cm/cm
Shore hardness	R-scale	ASTM D-785	110
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	18.5kg/cm	ASTM D-648	110	°C
	Hot deformation temperature	18.5kg/cm	ASTM D-648	105	°C
		Hot deformation temperature	4.6kg/cm	ASTM D-648	119	°C
		Hot deformation temperature	Hot deformation temperature	4.6kg/cm	ASTM D-648	114	°C
UL flame retardant rating	1/8"	UL 94	HB	calss
UL flame retardant rating	UL flame retardant rating	1/16"	UL 94	HB	calss
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D-792	1.08	g/cc
Shrinkage rate		ASTM D-955	0.4-0.7	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.