Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.10 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 5.0to15 g/10min |
| Shrinkage rate | | ASTM D955 | 2.0 % |
| Shrinkage rate | | ASTM D955 | 2.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 95to97 |
| Shore hardness | | ASTM D2240 | 43to45 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Dynamic Properties | | | 0.0380 |
| Dynamic Properties | | | 4.53E+08 dynes/cm² |
| Dynamic Properties | | | 2.97E+08 dynes/cm² |
| Dynamic Properties | | | 0.0250 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 89.5 MPa |
| Wear resistance - DIN | | DIN 53516 | 27.0 mm³ |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 12.4 MPa |
| tensile strength | | ASTM D412 | 36.5 MPa |
| elongation | Break | ASTM D412 | 660 % |
| tear strength | | ASTM D470 | 34 kN/m |
| tear strength | | ASTM D470 | 35 kN/m |
| tear strength | Split | ASTM D470 | 44 kN/m |
| compression set | | ASTM D395B | 35 % |
| Shore hardness | | ASTM D2632 | 63 % |
| film | Test Condition | Test Method | Test Result |
|---|
| Tear resistance of pants | | ASTM D1938 | 67.1 N/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | -53.0 °C |
| vicat | | ASTM D1525 | 166 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.