Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 0.920to0.960 g/cm³ |
| melt mass-flow rate | | ISO 1133 | 1.8to2.4 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 72.0 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-2 |
| Hot filament ignition temperature | | VDE0471/2 | 960 °C |
| Hot filament ignition temperature | | VDE0471/2 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | >30.0 MPa |
| Tensile strain | Break | ISO 527-2 | >70 % |
| Flexural modulus | | ISO 178 | >1450 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | >6.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 87.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 53.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.