Polyester, TS Menzolit® BMC 3100
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 2.00 g/cm³ | |
| Shrinkage rate | DIN53464 | 0.0 % | |
| ISO2577 | -0.030 % | ||
| Water absorption rate | ISO62 | <0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO527-2 | 1.0 % | |
| Flexural modulus | Compression Molded | ISO178 | 11000 MPa |
| Bending stress | Compression Molded | ISO178 | 79.0 MPa |
| Poisson's ratio | 内部方法 | 0.30 | |
| MatrixCrazingStrain | 内部方法 | 0.30 % | |
| Tensile modulus | Compression Molded | ISO527-2 | 14000 MPa |
| Tensile stress | ISO527-2 | 25.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179 | 15 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/A | >150 °C | ||
| Continuous use temperature | 内部方法 | 190 °C | |
| Glass Transition Temperature | DSC | 185 °C | |
| ISO11359-2 | 1E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.