Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTMD955 | 0.30 % |
| density | | ASTMD792 | 1.53 g/cm³ |
| Shrinkage rate | | ASTMD955 | 0.30 % |
| Shrinkage rate | | ASTMD955 | 0.90 % |
| density | | ASTMD792 | 1.53 g/cm³ |
| Shrinkage rate | | ASTMD955 | 0.90 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 120 |
| Rockwell hardness | R-Scale | ASTMD785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| WeatherResistance | | ASTMD570 | 0.060 % |
| WeatherResistance | | ASTMD570 | 0.060 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ASTMD638 | 2.5 % |
| tensile strength | | ASTMD638 | 130 MPa |
| elongation | Break | ASTMD638 | 2.5 % |
| Flexural modulus | | ASTMD790 | 7500 MPa |
| bending strength | | ASTMD790 | 180 MPa |
| tensile strength | | ASTMD638 | 130 MPa |
| Flexural modulus | | ASTMD790 | 7500 MPa |
| bending strength | | ASTMD790 | 180 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 100 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 100 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+16 ohms·cm |
| Volume resistivity | | ASTMD257 | 1E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 220 °C |
| | ASTMD648 | 210 °C |
| | ASTMD648 | 220 °C |
| | ASTMD648 | 210 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.