PC Makrolon® 2805(蓝底)
55
- Properties:currencyMedium viscosityMedium viscosityFor general injection mol
- Usages:Industrial applicationsElectrical fieldElectronic fieldAutomotive sectorUsed for industrial accessoriesAutomotive electronic componentsElectronic and electrical accessories; ul certific
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | -- cm3/(10分钟) | |
| ISO 1133 | 9.5 cm3/(10分钟) | ||
| Shrinkage rate | ISO 294-4 | 0.65 % | |
| ISO 294-4 | 0.7 % |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.30 % | |
| ISO 62 | 0.12 % | ||
| density | ISO 1183 | 1200 kg/m2 |
| Specific properties of raw materials | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ISO 489 | 1.586 -- | |
| transmittance | ISO 13468-2 | 89 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ISO 527-1-2 | ＞50 % | |
| Breaking stress | ISO 527-1-2 | -- MPa | |
| fracture strain | ISO 527-1-2 | -- % | |
| Tensile creep modulus | ISO 899-1 | 2200 MPa | |
| ISO 899-1 | 1900 MPa | ||
| Flexural modulus | ISO 179 | 2400 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eU | N kJ/m² | |
| kJ/m² | 参照ISO 179/1eA 75P(C) | ||
| Impact strength of cantilever beam gap | kJ/m² | 参照ISO 180/1eA 85P(C) | |
| Maximum destructive power | ISO 6603-2 | 5400 N | |
| tensile strength | ISO 6603-2 | 60 J | |
| Tensile modulus | ISO 527-1-2 | 2400 MPa | |
| Tensile stress | ISO 527-1-2 | 66 MPa | |
| Tensile strain | ISO 527-1-2 | 6.1 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | IEC 60250 | 3.1 -- | |
| IEC 60250 | 3.0 -- | ||
| Dissipation Factor | IEC 60250 | 5 10-4 | |
| IEC 60250 | 90 10-4 | ||
| Volume resistivity | IEC 60093 | 1E+14 Ohm.m | |
| Surface Resistivity | IEC 60093 | 1E+16 Ohm | |
| dielectric strength | IEC 60243-1 | 34 kv/毫米 | |
| Compared to the Leakage Traceability Index (CTI) | IEC 60112 | 250 等级 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Transition Temperature | ISO 11357-1-2 | 145 ℃ | |
| vicat | ISO 306 | 145 ℃ | |
| Linear coefficient of thermal expansion | ISO 11359-1-2 | 0.65 10-4/K | |
| ISO 11359-1-2 | 0.65 10-4/K | ||
| UL flame retardant rating | UL 94 | V-2 级 | |
| UL 94 | HB(2.5) 级 | ||
| UL 94 | 级 | ||
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| Glow wire combustion index (GWFI) | IEC 60695-2-12 | 850 ℃ | |
| IEC 60695-2-12 | 930 ℃ | ||
| Glow wire ignition temperature (GWIT) | IEC 60695-2-13 | 875 ℃ | |
| IEC 60695-2-13 | 875 ℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.