PA6 VOLGAMID® G30HSLBK201
84
- Properties:Dimensional stabilityHigh rigidityThermal stability30% glass fiber reinforceEnhanced levelPhotostabilityThermal stabilityGranularPolyamide 66/6+30% glass
- Usages:Fitness equipmentAutomotive Applications
CompareTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.36 g/cm³ | |
| ash content | ISO3451-4 | 30-33 % | |
| Water absorption rate | ISO 62 | -- % | |
| Moulding shrinkage | ISO294-4 | 0.3 / 0.8 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO527, 50mm/min | 185 Mpa | |
| elongation | ISO527, 50mm/min | 2 % | |
| Flexural modulus | 4.55 | 9000 Mpa | |
| bending strength | 4.55 | 260 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 12 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179 | 85 kJ/m² | |
| Rockwell hardness | ISO2039/2 | -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO 75 | 235 °C | ||
| UL Vertical Combustion | UL-94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.