Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.50 -- |
| Shrinkage rate | | % | 0.10 -- |
| Water absorption rate | | % | 0.80 -- |
| Water absorption rate | | % | 0.40 -- |
| density | | g/cm³ | 1.47 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore Hardness | | | -- 86 |
| Ball Indentation Hardness | | MPa | -- 190 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 13500 12500 |
| Tensile stress | Break | MPa | 170 160 |
| Tensile strain | Break | % | 5.0 5.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 14 14 |
| Charpy Notched Impact Strength | | kJ/m² | 18 18 |
| Impact strength of simply supported beam without notch | | kJ/m² | 95 90 |
| Impact strength of simply supported beam without notch | | kJ/m² | 95 90 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | -- 1E+12 |
| dielectric strength | | kV/mm | -- 40 |
| CTI | | V | -- 60.0 |
| Surface Resistivity | | ohms | -- 1E+11 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | °C | 90.0到120 -- |
| Continuous use temperature | | °C | 150 -- |
| melting temperature | | °C | 178 -- |
| Linear thermal expansion coefficient | | cm/cm/°C | 1.5E-05 -- |
| Linear thermal expansion coefficient | | cm/cm/°C | 9E-05 -- |
| Heat Deflection Temperature | | °C | 160 -- |
| Heat Deflection Temperature | | °C | 110 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.