PE蜡 H108
7
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | GB/T2914 | 0.02 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | GB/T1040 | 120 Mpa | |
| elongation at break | GB/T1040 | 0.8 % | |
| bending strength | GB/T9341 | 180 Mpa | |
| Flexural modulus | GB/T9341 | 1.8×10000 Mpa | |
| Impact strength of cantilever beam gap | GB/T1843 | 5 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | GB/T1033 | 2.0 g/cm³ | |
| Mold Shrinkage | GB/T15585 | 0.25/0.60 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | 1 ×10¹⁵Q.m | ||
| Surface Resistivity | 1 ×10¹⁴Q | ||
| Dielectric constant 1MHz | GB/T1409 | 4 | |
| electric strength | GB/T1408 | 16 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting point | GB/T4608 | 280 PC | |
| Hot deformation temperature (1.8MPa) | GB/T1634 | 260 PC | |
| Flame retardancy | GB/TUL94 | V-0 | |
| thermal conductivity | ASTME1461 | 5.0 w/mk |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.