Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| viscosity number | | cm³/g | 138to247 |
| balance | | % | 2.5 |
| melt mass-flow rate | | g/10min | 1.2-5.0 |
| flow | | mm/mm | 152.4E-3-0.635 |
| saturation | | % | 9.0 |
| Apparent density | | g/cm³ | 0.70-0.78 |
| saturation | | % | 7,9到11 |
| balance | | % | 2.5-3.5 |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | | 45.03to201.38 Mpa |
| Shore hardness | | | 77to80 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | % | 21to28 |
| Burning wire flammability index | | °C | 954to960 |
| Hot filament ignition temperature | | °C | 743to960 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield | | | 39.03to89.66 Mpa |
| coefficient of friction | | | 0.30-1.0 |
| fracture | | | 79.31to84.83 Mpa |
| fracture | | % | 2,2到12 |
| fracture | | | 40.0to171.72 Mpa |
| fracture | | % | 3,0到77 |
| Nominal tensile fracture strain | | % | 5,6到50 |
| Tensile modulus | | | 477.24到0.01,0.04E0.05 Mpa |
| yield | | % | 3,0到21 |
| yield | | | 64.76to85.52 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 0.556to4.643 |
| Impact strength of cantilever beam gap | | kJ/m² | 1.988to6.176 |
| Impact strength of simply supported beam without notch | | kJ/m² | 10.679to23.215 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Dissipation Factor | | | 0.020-0.30 |
| Volume resistivity | | | 3.50 |
| Surface Resistivity | | ohms | 1.0E+2-2.5E+13 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| horizontal | | mm/mm/°C | 99.1E-5-203.2E-5 |
| vicat | | °C | 67to247 |
| flow | | mm/mm/°C | 99.1E-5-101.6E-5 |
| Continuous use temperature | | °C | 87to202 |
| flow | | mm/mm/°C | 96.5E-5-152.4E-5 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.