Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D570 | 0.40 % |
| Shrinkage rate | | ASTM D955 | 0.20 % |
| density | | ASTM D792 | 1.51 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTM D785 | 98 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 75 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 186 MPa |
| Flexural modulus | | ASTM D790 | 5520 MPa |
| elongation | Break | ASTM D638 | 2.9 % |
| tensile strength | Break | ASTM D638 | 133 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 18 kV/mm |
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 3.2E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 207 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.