ASA KIBILAC® PW-997 TAIWAN CHIMEI
401
- Properties:UV resistanceWeather resistance
- Usages:Automotive sector
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO1183 | 1.07 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) | 220°C/10.0kg | ISO1133 | 7.00 | cm3/10min |
| Shrinkage rate | ISO294-4 | 0.40to0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 屈服 | ISO527-2/50 | 46.0 | Mpa |
| 断裂 | ISO527-2/50 | 34.0 | Mpa | |
| elongation | 断裂 | ISO527-2/50 | 25 | % |
| Bending modulus | ISO178 | 2100 | Mpa | |
| bending strength | ISO178 | 66.0 | Mpa | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 10 | kJ/m² |
| 23°C | ISO179 | 21 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 9.0 | kJ/m² |
| 23°C | ISO180/1A | 20 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ISO306/A120 | 109 | °C |
| Hot deformation temperature | 1.8MPa,未退火 | ISO75-2/A | 81.0 | °C |
| 1.8MPa,退火 | ISO75-2/A | 98.0 | °C | |
| vicat softening point | -- | ISO306/A50 | 106 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 9.3E-05 | cm/cm/°C |
| vicat softening point | -- | ISO306/B50 | 94.0 | °C |
| -- | ISO306/B120 | 97.0 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.