Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.18 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 62 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| atomization | | GM9305P | 83.0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ArizonaWeathering-DeltaE | | SAEJ1976 | 1.06(black) |
| FloridaWeathering-DeltaE | | SAEJ1976 | 1.96(black) |
| ozone resistance | | ISO 1431-1 | Pass |
| WeatherResistance | | SAEJ1960 | 0.800(black) |
| WeatherResistance | | SAEJ1885 | 1.30(black) |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 6.00 MPa |
| tensile strength | | ASTM D412 | 5.60 MPa |
| elongation | | ASTM D412 | 690 % |
| elongation | | ASTM D412 | 550 % |
| tear strength | | ASTM D624 | 26.5 kN/m |
| Shore hardness | | ASTM D2240 | 59 |
| tensile strength | | ASTM D412 | 1.90 MPa |
| tensile strength | | ASTM D412 | 2.50 MPa |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 37 | >2.00 MPa |
| tensile strength | Break | ISO 37 | >7.90 MPa |
| elongation | Break | ISO 37 | >630 % |
| tear strength | | ISO 34-1 | >31 kN/m |
| compression set | | ISO 815 | >28 % |
| compression set | | ISO 815 | >16 % |
| aging | Test Condition | Test Method | Test Result |
|---|
| Change rate of tensile strength in air | | SAEJ2236 | 9.0 % |
| elongation at break | | SAEJ2236 | 0.20 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| brittle temperature | | ISO 812 | <-54.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.