Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.90到2.10 g/cm³ |
| Water absorption rate | | ISO62 | <0.50 % |
| Apparent density | | ISO60 | 0.75到1.00 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.40到0.70 % |
| Shrinkage rate | | ISO2577 | 0.20到0.50 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 930 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >10.0 MPa |
| CompressionMoldingTemperature | | | 165到180 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 40.0到70.0 MPa |
| Flexural modulus | Compression Molded | ISO178 | 8000到12000 MPa |
| Flexural modulus | Injection | ISO178 | 8000到12000 MPa |
| Bending stress | Compression Molded | ISO178 | 80.0到100 MPa |
| Bending stress | Injection | ISO178 | 100到120 MPa |
| compression stress | | ISO604 | 150到200 MPa |
| Tensile modulus | Compression Molded | ISO527-2 | 6000到9000 MPa |
| Tensile modulus | Injection | ISO527-2 | 6000到9000 MPa |
| Tensile stress | | ISO527-2 | 35.0到60.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 2.5到3.5 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 3.0到4.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 5.0到10 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 8.0到11 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1.0E+12到1.0E+13 ohms |
| Volume resistivity | | IEC60093 | 1.0E+13到1.0E+14 ohms·cm |
| dielectric strength | | IEC60243-1 | 25到35 kV/mm |
| | IEC60250 | 6.005.00 |
| | IEC60250 | 5.004.00 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.90到1.1 W/m/K |
| maximum service temperature | | IEC60216 | 210 °C |
| maximum service temperature | | IEC60216 | 180 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.