Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 0.50 -- |
| Shrinkage rate | | % | 0.10 -- |
| Water absorption rate | | % | 1.1 -- |
| Water absorption rate | | % | 0.60 -- |
| density | | g/cm³ | 1.19 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 82 82 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 6000 5800 |
| tensile strength | Break | MPa | 115 110 |
| Tensile strain | Break | % | 3.0 3.0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 9.0 8.0 |
| Charpy Notched Impact Strength | | kJ/m² | 15 11 |
| Impact strength of simply supported beam without notch | | kJ/m² | 75 60 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | -- 1E+12 |
| Volume resistivity | | ohms·cm | 1E+11 1E+11 |
| dielectric strength | | kV/mm | 32 32 |
| Compared to the Leakage Tracking Index (CTI) | | V | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 140 -- |
| Heat distortion temperature | | °C | 65.0 -- |
| Continuous use temperature | | °C | 90.0to110 -- |
| Continuous use temperature | | °C | 140 -- |
| melting temperature | | °C | 178 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 3E-05 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.1E-04 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.