ABS/PMMA XYRON™ AT-30 BK ASAHI JAPAN
653
- Properties:transparentChemical resistance
- Usages:CastersAutomotive Applications
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO 1183 | 1.12 | g/cm | |
| Melt mass flow rate | 220℃/5kg | ISO 1133 | 15 | g/10min |
| Shrinkage rate | Flow | ASTM D-955 | 0.40-0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2650 | Mpa | |
| Yield stress | ISO 527-2 | 52.0 | Mpa | |
| Bending modulus | ISO 178 | 2600 | Mpa | |
| bending strength | ISO 178 | 81.0 | Mpa | |
| Impact strength of simply supported beam gap | ISO 179 | 10.00 | KJ/m | |
| Impact strength of cantilever beam gap | ASTM D-256 | 118 | J/m | |
| Rockwell hardness | ISO 2039-2 | 116 | R scale | |
| ISO 2039-2 | 65 | M Scale |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.80MPa，未退火 | ISO 75-2/A | 78.0 | °C |
| vicat softening point | ISO 306 | 101 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.