Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.12 -- |
| Shrinkage rate | | % | 0.70 -- |
| Shrinkage rate | | % | 0.30 -- |
| Water absorption rate | | % | 1.3 -- |
| Water absorption rate | | % | 0.80 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 74 -- |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 15 -- |
| Impact strength of simply supported beam without notch | | kJ/m² | 75 -- |
| Impact strength of simply supported beam without notch | | kJ/m² | 75 -- |
| Charpy Notched Impact Strength | | kJ/m² | 10 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | % | 8.0 10 |
| Tensile modulus | | MPa | 3500 3000 |
| tensile strength | Break | MPa | 80.0 70.0 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| Surface Resistivity | | ohms | -- 1E+12 |
| Volume resistivity | | ohms·cm | -- 1E+13 |
| dielectric strength | | kV/mm | 35 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 150 -- |
| Heat distortion temperature | | °C | 80.0 -- |
| Continuous use temperature | | °C | 90.0to120 -- |
| Continuous use temperature | | °C | 150 -- |
| melting temperature | | °C | 178 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 4E-05 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 8E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare