Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTMD570 | 0.40 % |
| Water absorption rate | Saturation | ASTMD570 | 1.3 % |
| density | | ASTMD792 | 1.40 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| PressureVelocity | | 内部方法 | 1.14 MPa·m/s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 4020 MPa |
| tensile strength | Ultimate | ASTMD638 | 110 MPa |
| elongation | Break | ASTMD638 | 4.0 % |
| Flexural modulus | | ASTMD790 | 4140 MPa |
| bending strength | Yield | ASTMD790 | 138 MPa |
| Compression Modulus | | ASTMD695 | 3100 MPa |
| compressive strength | | ASTMD695 | 165 MPa |
| Steel - Static | 内部方法 | 0.23 |
| Wear factor | | ASTMD3702 | 100 10^-8mm³/N·m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256A | 75 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTMD149 | 28 kV/mm |
| Surface Resistivity | | 内部方法 | >1.0E+13 ohms |
| dielectric constant | | ASTMD150 | 3.41 |
| Dissipation Factor | | ASTMD150 | 3.8E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 360 °C |
| Maximum operating temperature LongTerm, Air | | | 304 °C |
| Glass Transition Temperature | | ASTMD3418 | 323 °C |
| | ASTME831 | 4.9E-05 cm/cm/°C |
| thermal conductivity | | ASTMF433 | 0.22 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.