Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.03 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 1.8 g/10min |
| melt mass-flow rate | | ASTMD1238 | 18 g/10min |
| Shrinkage rate | | ASTMD955 | <0.40 % |
| Water absorption rate | | ASTMD570 | <0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| FlameRating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 250 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 220 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 39.3 Mpa |
| Tensile strength 2 | | ASTMD638 | 34.5 Mpa |
| elongation | | ASTMD638 | 30 % |
| Flexural modulus | | ASTMD790 | 2340 Mpa |
| bending strength | | ASTMD790 | 68.9 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| High arc combustion index (HAI) | | UL746 | 200 |
| High voltage arc ignition resistance index | | UL746 | 0.00 mm/min |
| Hot-wireIgnition | | UL746 | 17 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 82.0 °C |
| vicat | | ASTMD15254 | 100 °C |
| RTI Elec | | UL746 | 60.0 °C |
| RTI Imp | | UL746 | 60.0 °C |
| RTI Str | | UL746 | 60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.