PP 7032E3 EXXONMOBIL SINGAPORE

190

Form：Granules | Grade：Injection grade

Properties:

Block copolymerHigh mobilityHigh rigidityHigh impact resistance

Typical Applications:

Household appliancessmall home appliancesLighting fixtureschipcontainerToyIndustrial containersShell

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Household appliances \| small home appliances \| Lighting fixtures \| chip \| container \| Toy \| Industrial containers \| Shell
Properties:	Block copolymer \| High mobility \| High rigidity \| High impact resistance

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	6.8	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	57	kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256A	无断裂
	Impact strength of cantilever beam gap	-40°C	ISO 180/1A	9.0	kJ/m²
		Impact strength of cantilever beam gap	-18°C	ISO 180/1A	11	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	53	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1	1200	Mpa
tensile strength	Yield3	ASTM D638	23.7	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	23.0	Mpa
elongation	Yield3	ASTM D638	6.0	%
elongation	elongation	Yield	ISO 527-2/50	5.6	%
Bending modulus	1% Secant 4	ASTM D790A	1210	Mpa
	Bending modulus	1% Secant 5	ASTM D790B	1300	Mpa
	Bending modulus	Bending modulus	--6	ISO 178	1140	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ASTM D648	90.6	°C
	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	82.0	°C
		Hot deformation temperature	0.45 MPa, Annealed	ASTM D648	112	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	50.2	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ExxonMobil Method	0.900	g/cm³
melt mass-flow rate	230°C/2.16 kg	ASTM D1238	4.0	g/10 min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ASTM D785	84

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.