Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.70 g/cm³ |
| Shrinkage rate | | ISO2577 | 1.5 % |
| Shrinkage rate | | ISO294-4 | 0.050 % |
| Shrinkage rate | | ISO2577 | 0.35 % |
| Shrinkage rate | | ISO2577 | 0.040 % |
| Water absorption rate | | ISO62 | 5.5 % |
| Water absorption rate | | ISO62 | 2.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 230 Mpa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 600 °C |
| Extreme Oxygen Index 7 | | ISO4589-2 | 23 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ISO Shortcut | | ISO1874 | PA66,GR,14-110,GF30 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 179 Mpa |
| Tensile stress | | ISO527-2/5 | 185 Mpa |
| elongation | | ASTMD638 | 3.0 % |
| Tensile strain | | ISO527-2/5 | 3.0 % |
| Flexural modulus | | ASTMD790 | 841 Mpa |
| Flexural modulus | | ISO178/A | 8400 Mpa |
| bending strength | | ASTMD790 | 290 Mpa |
| Bending stress | | ISO178/A | -- Mpa |
| Bending stress | | ISO178 | 290 Mpa |
| Bending stress | | | 4.0 % |
| Tensile modulus | | ASTMD638 | 10300 Mpa |
| Tensile modulus | | ISO527-2/1 | 10600 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 70 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 90 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+14 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | | IEC60243-1 | 40 KV/mm |
| | IEC60250 | 4.00 |
| | IEC60250 | 4.00 |
| Dissipation Factor | | IEC60250 | 9E-03 |
| Dissipation Factor | | IEC60250 | 0.018 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO306/B120 | >230 °C |
| Melting temperature 5 | | ISO11357-3 | 263 °C |
| | ISO11359-2 | 2.5E-05 cm/cm/°C |
| | ISO11359-2 | 1E-04 cm/cm/°C |
| | ISO75-2/B | 250 °C |
| | ISO75-2/A | 250 °C |
| | ISO75-2/C | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.