PA66 Vydyne® 20NSP

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.14 g/cm³
Shrinkage rate		ISO 294-4	1.6 %
Shrinkage rate	Shrinkage rate		ISO 294-4	1.4 %
Water absorption rate		ISO 62	1.2 %
Water absorption rate	Water absorption rate		ISO 62	2.4 %
Outdoor applicability		UL 746C	f2

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature		IEC 60695-2-13	825 °C
	Hot filament ignition temperature		IEC 60695-2-13	850 °C
		Hot filament ignition temperature		IEC 60695-2-13	850 °C
		Hot filament ignition temperature	Hot filament ignition temperature		IEC 60695-2-13	850 °C
Limiting Oxygen Index		ISO 4589-2	26 %
Burning wire flammability index		IEC 60695-2-12	960 °C
UL flame retardant rating		UL 94	V-2
	UL flame retardant rating		UL 94	V-2
		UL flame retardant rating		UL 94	V-2
		UL flame retardant rating	UL flame retardant rating		UL 94	V-2
Burning wire flammability index		IEC 60695-2-12	960 °C
	Burning wire flammability index		IEC 60695-2-12	960 °C
	Burning wire flammability index	Burning wire flammability index		IEC 60695-2-12	960 °C

Mechanical properties	Test Method	Test Result
tensile strength	ISO 527-2	75.0 MPa
Tensile strain	ISO 527-2	5.0 %
Nominal tensile fracture strain	ISO 527-2	13 %
Flexural modulus	ISO 178	3200 MPa
bending strength	ISO 178	100 MPa
Poisson's ratio	ISO 527-2	0.40
Tensile modulus	ISO 527-2	3800 MPa
tensile strength	ISO 527-2	95.0 MPa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap		ISO 180	5.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180	6.0 kJ/m²
Charpy Notched Impact Strength		ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	6.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	NoBreak

Electrical performance	Test Condition	Test Method	Test Result
High arc combustion index (HAI)		UL 746	PLC 0
High arc combustion index (HAI)	High arc combustion index (HAI)		UL 746	PLC 0
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 0
Hot wire ignition (HWI)		UL 746	PLC 4
Volume resistivity		IEC 60093	1E+13 ohms·cm
dielectric strength		IEC 60243	26 kV/mm
arc resistance		ASTM D495	PLC 5
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0
High arc combustion index (HAI)		UL 746	PLC 1
High arc combustion index (HAI)	High arc combustion index (HAI)		UL 746	PLC 0
Hot wire ignition (HWI)		UL 746	PLC 4
	Hot wire ignition (HWI)		UL 746	PLC 3
	Hot wire ignition (HWI)	Hot wire ignition (HWI)		UL 746	PLC 2

Thermal performance	Test Condition	Test Method	Test Result
		ISO 11359-2	1E-04 cm/cm/°C
RTI Elec		UL 746	130 °C
	RTI Elec		UL 746	130 °C
		RTI Elec		UL 746	130 °C
		RTI Elec	RTI Elec		UL 746	130 °C
RTI Imp		UL 746	75.0 °C
Hot deformation temperature (HDT)		ISO 75-2/B	230 °C
Hot deformation temperature (HDT)	Hot deformation temperature (HDT)		ISO 75-2/A	90.0 °C
melting temperature		ISO 11357-3	260 °C
		ISO 11359-2	1E-04 cm/cm/°C
RTI Imp		UL 746	75.0 °C
	RTI Imp		UL 746	75.0 °C
	RTI Imp	RTI Imp		UL 746	75.0 °C
RTI Str		UL 746	75.0 °C
	RTI Str		UL 746	85.0 °C
		RTI Str		UL 746	85.0 °C
		RTI Str	RTI Str		UL 746	85.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.