PA6

PA6 SOLLAMID B 2700 - B 2710 Krisoll Resinas Plásticas Ltda.

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	J/m	55 140

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm		HB --

mechanical properties	Test Condition	Test Method	Test Result
elongation	Break,23°C	%	50to100 250到300
tensile strength	23°C	MPa	75.0 40.0
Tensile modulus	23°C	MPa	2900 1100
bending strength	23°C	MPa	95.0 40.0
Bending modulus	23°C	MPa	2800 1000

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	cm/cm/°C	7E-05 --
Melting temperature		°C	214to220 --
Hot deformation temperature	1.8MPa,Unannealed	°C	65.0 --
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	°C	180 --

Physical properties	Test Condition	Test Method	Test Result
density		g/cm³	1.14 --
thermal stability		°C	80 --
Water absorption rate	23°C,24hr	%	1.5 --
Shrinkage rate	MD	%	1.2to1.6 --
melt mass-flow rate		g/10min	15to35 --

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength		kV/mm	21 --
Volume resistivity		ohms·cm	1E+15 --

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale,23°C		120 103

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.