Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.51 g/cm³ |
| Shrinkage rate | | ASTM D955 | 0.10 % |
| Water absorption rate | | ASTM D570 | 0.16 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 122 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | Yield | ASTM D790 | 324 MPa |
| compressive strength | | ASTM D695 | 152 MPa |
| Tensile modulus | | ASTM D638 | 13100 MPa |
| tensile strength | Yield | ASTM D638 | 221 MPa |
| tensile strength | | ASTM D638 | 207 MPa |
| elongation | Break | ASTM D638 | 2.5 % |
| Flexural modulus | | ASTM D790 | 11700 MPa |
| bending strength | | ASTM D790 | 303 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 120 J/m |
| Suspended wall beam without notch impact strength | | ASTM D4812 | 1100 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+14 ohms·cm |
| dielectric strength | | ASTM D149 | 20 kV/mm |
| dielectric constant | | ASTM D150 | 3.90 |
| Dissipation Factor | | ASTM D150 | 0.018 |
| arc resistance | | ASTM D495 | 100 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 149 °C |
| Heat distortion temperature | | ASTM D648 | 143 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 2.3E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.58 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.