Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 2.14 g/cm³ |
| melt mass-flow rate | | ASTM D3307 | 2.0 g/10min |
| melt mass-flow rate | | ISO 12086 | 2.0 g/10min |
| Water absorption rate | | ASTM D570 | <0.030 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 55 |
| Shore hardness | | ISO 868 | 55 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Limiting Oxygen Index | | ASTM D2863 | >95 % |
| Limiting Oxygen Index | | ISO 4589-2 | >95 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| MITFoldingEndurance | | ASTM D2176 | 5E+05 Cycles |
| critical shear rate | | | 12.0 sec^-1 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 12086 | 28.0 MPa |
| tensile strength | | ISO 12086 | 14.0 MPa |
| elongation | | ASTM D3307 | 300 % |
| elongation | | ASTM D3307 | 500 % |
| Tensile strain | | ISO 12086 | 300 % |
| Tensile strain | | ISO 12086 | 500 % |
| Flexural modulus | | ASTM D790 | 625 MPa |
| Flexural modulus | | ASTM D790 | 69.0 MPa |
| Flexural modulus | | ISO 178 | 625 MPa |
| Flexural modulus | | ISO 178 | 69.0 MPa |
| tensile strength | | ASTM D3307 | 28.0 MPa |
| tensile strength | | ASTM D3307 | 14.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 80 kV/mm |
| dielectric strength | | IEC 60243-1 | 80 kV/mm |
| dielectric constant | | ASTM D150 | 2.03 |
| dielectric constant | | IEC 60250 | 2.03 |
| Dissipation Factor | | ASTM D150 | <2.0E-4 |
| Dissipation Factor | | IEC 60250 | <2.0E-4 |
| Volume resistivity | | ASTM D257 | 1E+18 ohms·cm |
| Volume resistivity | | ISO 1325 | 1E+18 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ASTM D4591 | 305 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.