PARA IXEF® BXT 2000
65
- Properties:Creep resistancehigh strength
- Usages:sporting goodsVehicle electronicsPipe fittingssheetPipeline systemfilmBlow molding applications
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Apparent density | ASTM D1895B | 0.70 g/cm³ | |
| melt mass-flow rate | 6.00 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 63.4 Mpa | |
| ISO 527-2 | 63.8 Mpa | ||
| ASTM D638 | 39.9 Mpa | ||
| Tensile modulus | ISO 527-2 | 2470 Mpa | |
| elongation | ASTM D638 | 4.0 % | |
| Tensile strain | ISO 527-2 | 3.7 % | |
| Nominal tensile fracture strain | ISO 527-2 | 77 % | |
| ModuleElasticity | ASTM D638 | 2.48 GPa | |
| elongation at break | ASTM D638 | 44 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180 | 190 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Permeation-CE10Fuel | SAEJ2659 | 0.83 g·mm/m²/atm/24hr |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 82.0 °C | |
| melting temperature | 230 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.