PA6 GFC 30 NATURAL
0
- Properties:Glass beads fiberglass30%filler by weightlubricatedthermally stablenucleated
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.34 to 1.36 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 0.60 % | |
| 0.30 | |||
| Water absorption rate | ISO 62 | 0.20 % | |
| ash content | ISO 3451 | 29 to 31 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hardness (Shore) | ISO 868 | 84 to 87 | |
| Tensile modulus | ISO 527-2 | 6500 to 7500 MPa | |
| Tensile strain | ISO 527-2 | 3.0 to 4.0 % | |
| Flexural modulus | ISO 178 | 5500 to 6000 MPa | |
| bending strength | ISO 178 | 140 to 160 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 7.0 to 10 kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180/1A | 7.0 to 10 kJ/m² | |
| tensile strength | ISO 527-2 | 130 to 150 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/B | 200 ℃ | |
| melting temperature | ISO 3146 | 215 to 225 ℃ | |
| UL flame retardant rating | UL 94 | HB | |
| Hot deformation temperature (HDT) | ISO 75-2/B | 215 ℃ | |
| ISO 75-2/A | 195 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.