Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO294-4 | 0.40到0.70 % |
| density | | ISO1183 | 1.08 g/cm³ |
| melt mass-flow rate | | ISO1133 | 8.0 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO2039-2 | 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 65 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180 | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179 | 12 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | ISO178 | 65.0 MPa |
| Tensile stress | | ISO527-2/50 | 50.0 MPa |
| Tensile strain | Break | ISO527-2/50 | 20 % |
| Flexural modulus | | ISO178 | 2300 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | | ISO75-2/A | 93.0 °C |
| vicat | | ISO306/B50 | 103 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.